Short Description:
Chemical name：1,3-Propanediamine, N,N-1,2-ethanediylbis-, reaction products with cyclohexane and peroxidized N-butyl-2,2,6,6-tetramethyl-4-piperidinamine-2,4,6-trichloro-1,3,5-triazine reaction products
CAS number： 191680-81-6
Molecular structure：
Appearance： Like white to light red to white crystalline particles solid
MELTING RANGE (℃)：108.00-123.00
FLASH POINT (℃)： ≥110
VOLATILE (%)： ≤0.50
TGA：1% weight loss temperature 260°C; 10% weight loss temperature 285°C
Application：
YIHOO NOR116 has very good polymer compatibility, high extraction resistance and aging resistance. It is a low alkalinity, monomer n-alkoxy hindered amine (NOR HALS). The low-alkaline YIHOO NOR116 provides flame retardancy, light and thermal stability for polyolefin fibers, narrow bands and films. It is a halogen-free flame retardant that does not react with hindered amine light stabilizers. Compared with traditional flame retardants, low levels of NOR116 are effective. It is suitable for melt processing without affecting the mechanical properties of the polymer.
Chemical name：1,3-Propanediamine, N,N-1,2-ethanediylbis-, reaction products with cyclohexane and peroxidized N-butyl-2,2,6,6-tetramethyl-4-piperidinamine-2,4,6-trichloro-1,3,5-triazine reaction products
CAS number： 191680-81-6
Appearance： Like white to light red to white crystalline particles solid
MELTING RANGE (℃)：108.00-123.00
FLASH POINT (℃)： ≥110
VOLATILE (%)： ≤0.50
TGA：1% weight loss temperature 260°C; 10% weight loss temperature 285°C
Application：
YIHOO NOR116 has very good polymer compatibility, high extraction resistance and aging resistance. It is a low alkalinity, monomer n-alkoxy hindered amine (NOR HALS). The low-alkaline YIHOO NOR116 provides flame retardancy, light and thermal stability for polyolefin fibers, narrow bands and films. It is a halogen-free flame retardant that does not react with hindered amine light stabilizers. Compared with traditional flame retardants, low levels of NOR116 are effective. It is suitable for melt processing without affecting the mechanical properties of the polymer.